LOCTITE® ABLESTIK 8008HT
Známé jako ABLECOAT 8008HT
Vlastnosti a výhody
LOCTITE ABLESTIK 8008HT, Proprietary Hybrid Chemistry, Die Attach
LOCTITE® ABLESTIK 8008HT adhesive is designed for high power devices in high UPH environment. It offers a lead-free alternative to soft solder and eutectic and can potentially reduce the layers of backside metallization required. This material can be applied to a wafer backside by stencil printing and then B-staged in an oven. The adhesive can then be cured after die attach in an in-line process exhibiting a consistent, void-free bondline without bleed. LOCTITE ABLESTIK 8008HT should be used with a pressure sensitive dicing tape and is not compatible with UV dicing tapes.
Oblasti Použití
Dokumenty ke stažení
Hledáte TS nebo BL v jiném jazyce?
Další dokumenty
Technické informace
| Aplikace | Připevnění formy |
| Barva | Stříbrná |
| Extrahovatelný iontový obsah, Chlorid (CI-) | 9.0 ppm |
| Extrahovatelný iontový obsah, Draslík (K+) | 9.0 ppm |
| Extrahovatelný iontový obsah, Sodík (Na+) | 9.0 ppm |
| Koeficient tepelné roztažnosti (CTE) | 37.0 ppm/°C |
| Koeficient tepelné roztažnosti (CTE), Above Tg | 62.0 ppm/°C |
| Modul v tahu, @ 250.0 °C | 2451.0 N/mm² (355340.0 psi ) |
| Objemový odpor | 0.00005 Ohm cm |
| Pevnost ve střihu RT, 2 x 2 mm Si die on Cu leadframe | 6.0 kg-f |
| Pevnost ve střihu za tepla, @ 260.0 °C 2 x 2 mm Si die on Cu LF | 2.6 kg-f |
| Plán vytvrzení, Snap Cure @ 170.0 °C | 20.0 sec. |
| Tepelná vodivost | 11.0 W/mK |
| Teplota skelného přechodu (Tg) | 264.0 °C |
| Tixotropní index | 4.0 |
| Viskozita, Brookfield CP51, @ 25.0 °C Speed 5 rpm | 50000.0 mPa.s (cP) |
| Způsob vytvrzování | Vytvrzování teplem |
LOCTITE® ABLESTIK 8008HT
LOCTITE ABLESTIK 8008HT, Proprietary Hybrid Chemistry, Die Attach