LOCTITE® STYCAST US 1195
Omadused ja eelised
LOCTITE STYCAST US 1195, Urethane, Potting and Encapsulating
LOCTITE® STYCAST US 1195 is formulated for potting electronics or devices for protection against environmental hazards. This material exhibits high hardness compared to other urethane materials allowing improved durability and impact resistance. It's low Tg allows for better thermal cycle performance to meet low temperature requirements in harsh environments. LOCTITE STYCAST US 1195 passed internal flammability testing at 3 mm thickness.
Lugege rohkem
Dokumendid ja allalaadimised
Otsite TDS-i või SDS-i teises keeles?
Tehniline teave
| Segatud | |
| Tihedus, Segatud | 1.43 g/cm³ |
| Viskoossus, Brookfield - RVF, Segatud @ 25.0 °C Spindle 51, speed 5.0 rpm | 19000.0 mPa.s (cP) |
| Värvus, Segatud | Must |
| Füüsiline vorm | Vedelik |
| Klaasistumistemperatuur (Tg) | -75.0 °C |
| Komponentide arv | 2-komponentne |
| Kõlblikkusaeg | 183.0 päev |
| Kõvenemisaeg, @ 65.0 °C | 4.0 tund |
| Mahu resistiivsus | 9.6x10¹⁴ Ohm cm |
| Rakendused | Kapseldamine |
| Seguvahekord, mahu järgi | 13.45 : 100 |
| Seguvahekord, massi järgi | 11.5 : 100 |
| Shore’i kõvadus, Shore A | 91.0 |
| Soojusjuhtivus | 0.67 W/mK |
| Soojuspaisumise koefitsient (CTE), Above Tg | 128.0 ppm/°C |
| Soojuspaisumise koefitsient (CTE), Below Tg | 58.0 ppm/°C |
| Säilitustemperatuur | 25.0 °C |
| Tahkumistüüp | Kuumkõvenemine |
| Vaik | |
| Tihedus, Vaik | 1.24 g/cm³ |
| Viskoossus, Brookfield - RVF, Vaik @ 25.0 °C | 55.0 mPa.s (cP) |
| Värvus, Vaik | Tumepruun |
| Tugevdaja | |
| Tihedus, Tugevdaja | 1.45 g/cm³ |
| Viskoossus, Brookfield - RVF, Tugevdaja @ 25.0 °C Spindle 51, speed 5.0 rpm | 40000.0 mPa.s (cP) |
| Värvus, Tugevdaja | Must |
LOCTITE® STYCAST US 1195
LOCTITE STYCAST US 1195, Urethane, Potting and Encapsulating